Cat.No ACM-IM-126
- Description
- Application
A non-reinforced per-fluorinated sulfonic acid (PFSA) / PTFE copolymer cation exchange membrane (CEM)
Direct methanol fuel cells (DMFC), electrolysis, redox-flow battery, using aqueous acidic conditions. Membrane is not stable under alkaline conditions.
| Backing Foil | PET Foil |
|---|---|
| Bubble Point | >4 bar (in H2O at 25°C) |
| Characteristics | Low resistance, high mechanical stability, and high stability in acidic environment. |
| Counter Ion | H-form |
| Delivery Condition | Dry (Delivery form) |
| Elongation At Break | >300% |
| Exchange Capacity | 0.6-0.8 meq/g |
| Membrane Appearance | Transparent/Colorless |
| Non-Std Modulus | 250-400 MPa |
| Permselectivity | >96% |
| pH | 0-10 pH (Stability Range at 25°C) |
| Reinforcement | None |
| Resistance | 0.2-0.3 (in H2O at 25°C in H-form) Ω·cm2 |
| Size | 20cm x 30cm |
| Specific Conductivity | 60-70 (in H2O at 25°C in H-form) mS·cm-1 |
| Swelling | 4-6% (in H2O at 25°C in H-form) (Dimensional Swelling) |
| Tensile Strength | 20-40 MPa (max.) |
| Thickness | 100-200 µm |
| Yield Strength | 10-20 MPa (at 23°C/50% R.H.) |